Aluminum Alloy: |
6061, 6063, 2024, 7050 |
Stainless Steel: |
||||
USA |
Japanese |
Germany |
||
ASTM/AISI |
UNS |
JIS |
DIN |
W-Nr |
304 |
S30400 |
SUS 304 |
X5CrNi18-10 |
1.4301 |
316 |
S31600 |
SUS 316 |
X5CrNiMo177-12-2 |
1.4401 |
410 |
S41000 |
SUS 410 |
X10Cr13 |
1.4024 |
630 |
S17400 |
SUS 630 |
X5CrNiCuNb17-4 |
1.4542 |
Tool steel: |
A-2, A-6, D-2, D-5, SKT4, SKD61, H13 |
Alloy Steel |
||||||
China |
USA |
Japanese |
Germany |
ISO |
||
GB |
ASTM/AISI |
UNS |
JIS |
DIN |
W-Nr |
|
42CrMo |
4140 |
G41400 |
SCM440 |
42CrMo4 |
1.7225 |
42CrMo4 |
40CrNiMo |
4340 |
G43400 |
SNCM439 |
36CrNiMo4 |
1.6511 |
36CrNiMo4 |
20CrNiMo |
8620 |
G86200 |
SNCM220 |
20CrNiMo2 |
1.6523 |
20CrNiMo2 |
Carbon Steel |
||||||
China |
USA |
Japanese |
Germany |
ISO |
||
GB |
ASTM/AISI |
UNS |
JIS |
DIN |
W-Nr |
|
15 |
1015 |
G10150 |
S15C |
C15E |
1.0401 |
C15E4 |
Ck15 |
1.1141 |
|||||
20 |
1020 |
G10200 |
S20C |
C22E |
1.0402 |
C20E4 |
Ck22 |
1.1151 |
|||||
25 |
1025 |
G10250 |
S25C |
C25E |
1.1158 |
C25E4 |
Ck25 |
||||||
30 |
1030 |
G10300 |
S30C |
C30E |
1.1178 |
C30E4 |
Ck30 |
||||||
35 |
1035 |
G10350 |
S35C |
C35E |
1.1181 |
C35E4 |
Ck35 |
||||||
40 |
1040 |
G10400 |
S40C |
C40E |
1.1186 |
C40E4 |
Ck40 |
||||||
45 |
1045 |
G10450 |
S45C |
C45E |
1.1191 |
C45E4 |
Ck45 |
||||||
50 |
1050 |
G10500 |
S50C |
C50E |
1.21 |
C50E4 |
Ck50 |
||||||
55 |
1055 |
G10550 |
S55C |
C55E |
1.1203 |
C55E4 |
Ck55 |
Cast steel comparison (or equivalent) |
||||||
China |
United States |
Japan |
Germany |
|||
China, GB |
ASTM |
AISI/UNS |
SAE |
JIS |
Din |
W-Nr. |
20 |
1020 |
G10200 |
1020 |
S20C |
Ck22 |
1.1151 |
S20CK |
||||||
45 |
1045 |
G10450 |
1045 |
S45C |
Ck45 |
1.1191 |
65Mn |
1566 |
G15660 |
1566(1066) |
S58C |
65M4 |
– |
20Cr |
5120 |
G51200 |
5120 |
SCr420 |
20Cr4 |
1.7027 |
40Cr |
5140 |
G51400 |
5140 |
SCr440 |
41Cr4 |
1.7035 |
35CrMo |
4135 |
G41350 |
4135 |
SCM435 |
34CrMo4 |
1.7220 |
42CrMo |
4140 |
G41400 |
4140 |
SCM440 |
42CrMo4 |
1.7225 |
40CrNiMo |
4340 |
G86200 |
8620 |
SNCM439 |
36CriNiMo4 |
1.6511 |
GCr15 |
5210 |
G52100 |
5210 |
SUJ2 |
100Cr6 |
1.3505 |
1Cr18Ni9Ti |
– |
– |
– |
– |
X10CrNiTi18 9 |
1.4541 |
Cast malleable iron comparison (or equivalent) |
||||
China GB/T9440-1988 |
ASTM A47 |
Japan JIS |
Germany |
ISO Standard |
DIN(W-Nr.) |
||||
KTH300-06 |
– |
FCMB30-06 |
– |
B30-06 |
FCMB27-05 |
||||
KTH330-08 |
22010 |
FCMB31-08 |
– |
– |
KTH350-10 |
32510 |
FCMB35-10 |
GTS-35-10 0.8135 |
B35-10 |
KTH370-12 |
35018 |
(FCMB37) |
– |
– |
Cast ductile iron comparison (or equivalent) |
||||||
China GB/T1348-1988 |
ASTM A536-99 |
UNS |
Japan JIS |
Germany |
ISO1083:1987 |
|
Din |
W-Nr. |
|||||
QT400-18 |
60-40-18 |
F32800 |
FCD400-18 |
GGG-40 |
0.7040 |
400-18 |
QT400-15 |
60-42-10 |
– |
FCD400-15 |
GGG-40 |
0.7040 |
400-15 |
QT450-10 |
65-45-12 |
F33100 |
FCD450-10 |
– |
– |
450-10 |
QT500-7 |
70-50-05 |
– |
FCD500-7 |
GGG-50 |
0.7050 |
500-7 |
QT600-3 |
80-60-03 |
– |
FCD600-3 |
GGG-60 |
0.7060 |
600-3 |
Cast gray iron comparison (or equivalent) |
|||||||
China GB/T 9439-1988 |
ASTM A159-82 |
UNS |
ASTM A48-00 |
Japan JIS |
Germany |
ISO Standard |
|
Din |
W-Nr. |
||||||
HT100 |
– |
– |
– |
FC100 |
GG10 |
0.6010 |
100 |
HT150 |
G1800 |
F11701 |
No. 20 |
FC150 |
GG15 |
0.6015 |
150 |
HT200 |
G2500 |
F12101 |
No. 30 |
FC200 |
GG20 |
0.6020 |
200 |
HT250 |
G3000 |
F12401 |
No. 35 |
FC250 |
GG25 |
0.6025 |
250 |
F12801 |
No. 40 |
||||||
HT300 |
G3500 |
F13301 |
No. 45 |
FC300 |
GG30 |
0.6030 |
300 |
HT350 |
G4000 |
F13501 |
No. 50 |
FC350 |
GG35 |
0.6035 |
350 |
Die casting alloy properties |
Aluminum die casting alloys |
Zinc-aluminum cast alloys |
Zinc casting alloys |
Magnesium die casting alloys |
||||||||
|
A360 |
A380 |
A383 |
A413 |
ZA-8 |
ZA-27 |
Zamak 3 |
Zamak 5 |
AZ91D |
AM60B |
AM50A |
AZ63 |
Ultimate Tensile Strength, MPa (ksi) |
300 (44) |
317(46) |
310(45) |
296 (43) |
374(54.2) |
426(61.8) |
285(41.3) |
328(47.6) |
230(33.4) |
24(35) |
228(33) |
275(39.9) |
Tensile Yield Strength, MPa (ksi) |
170 (24.7) |
159(23) |
152 (22) |
145 (21) |
290(42.1) |
371(53.8) |
|
|
150(21.8) |
131(19) |
124(18) |
130(18.9) |
Elongation (% in.2 in.) |
2.5 |
2.5 |
3.5 |
2.5 |
8 |
2.5 |
10 |
7 |
3 |
13 |
15 |
5 |
Shear Strength, MPa (ksi) |
190 (28) |
195 (28) |
187 (27) |
170 (25) |
275(39.9) |
325(47.1) |
215(31.2) |
262(38) |
140(20) |
241(35) |
228 (33) |
145(21) |
Hardness, Brinell |
75 |
80 |
75 |
80 |
103 |
119 |
82 |
91 |
63 |
65 |
60 |
73 |
Thermal Conductivity, |
113 (784) |
109 (756) |
96.2(668) |
121 (840) |
115(798) |
125(868) |
113(784) |
62.9(437) |
72.7(505) |
61(423) |
65(451) |
61(423) |
Density, g/cc (lb/in³) |
2.68(0.097) |
2.76 (0.1) |
2.70(0.098) |
2.66(0.0961) |
6.3(0.228) |
5.02(0.181) |
6.6(0.238) |
6.6(0.24) |
1.8(0.0654) |
1.8(0.0650) |
1.77(0.0639) |
1.83(0.0661) |
Chemical Properties |
|
|
|
|
|
|
|
|
|
|
|
|
Aluminum, Al |
85.1-90.6% |
79.6-89.5% |
79.7-88.5% |
82.2-89.0% |
8% |
27% |
4.10% |
4.20% |
8.5%-9.5% |
5.6%-6.4% |
4.5%-5.3% |
5.3%-6.7% |
Copper, Cu |
<=0.60% |
3.0-4.0% |
2.0-3.0% |
<=1.0% |
|
2.20% |
|
|
<=0.025 |
<=0.008 |
<=0.008 |
<=0.02 |
Iron, Fe |
<=2.0% |
<=2.0% |
<=1.30% |
<=2.0% |
|
|
|
|
<=0.004 |
<=0.004 |
<=0.004 |
<=0.003 |
Magnesium, Mg |
0.40 -0.60% |
<=0.10% |
<=0.10% |
<=0.10% |
0.02% |
0.02% |
0.04% |
0.03% -0.06% |
|
|
|
|
Manganese, Mn |
<=0.35% |
<=0.50% |
<=0.50% |
<=0.35% |
|
|
|
|
0.17%-0.4% |
0.26%-0.5% |
0.28%-0.5% |
0.15%-0.17% |
Nickel, Ni |
<=0.50% |
<=0.50% |
<=0.30% |
<=0.50% |
|
|
|
|
<=0.001% |
<=0.001% |
<=0.001% |
<=0.002% |
Other, total |
<=0.25% |
<=0.50% |
<=0.50% |
<=0.25% |
|
|
|
|
|
|
|
|
Silicon, Si |
9.0-10.0% |
7.50-9.50% |
9.50-11.5% |
11.0-13.0% |
|
|
|
|
<=0.08% |
<=0.08% |
<=0.08% |
<=0.1% |
Tin, Sn |
<=0.15% |
<=0.35% |
<=0.15% |
<=0.15% |
|
|
|
|
|
|
|
|
Zinc, Zn |
<=0.50% |
<=3.0% |
<=3.0% |
<=0.50% |
91% |
71% |
96% |
95% |
0.45% -0.9% |
<=0.2% |
<=0.2% |
2.5%-3.5% |
Quality Management System Certificate
Aluminum Alloy: |
6061, 6063, 2024, 7050 |
Stainless Steel: |
||||
USA |
Japanese |
Germany |
||
ASTM/AISI |
UNS |
JIS |
DIN |
W-Nr |
304 |
S30400 |
SUS 304 |
X5CrNi18-10 |
1.4301 |
316 |
S31600 |
SUS 316 |
X5CrNiMo177-12-2 |
1.4401 |
410 |
S41000 |
SUS 410 |
X10Cr13 |
1.4024 |
630 |
S17400 |
SUS 630 |
X5CrNiCuNb17-4 |
1.4542 |
Tool steel: |
A-2, A-6, D-2, D-5, SKT4, SKD61, H13 |
Alloy Steel |
||||||
China |
USA |
Japanese |
Germany |
ISO |
||
GB |
ASTM/AISI |
UNS |
JIS |
DIN |
W-Nr |
|
42CrMo |
4140 |
G41400 |
SCM440 |
42CrMo4 |
1.7225 |
42CrMo4 |
40CrNiMo |
4340 |
G43400 |
SNCM439 |
36CrNiMo4 |
1.6511 |
36CrNiMo4 |
20CrNiMo |
8620 |
G86200 |
SNCM220 |
20CrNiMo2 |
1.6523 |
20CrNiMo2 |
Carbon Steel |
||||||
China |
USA |
Japanese |
Germany |
ISO |
||
GB |
ASTM/AISI |
UNS |
JIS |
DIN |
W-Nr |
|
15 |
1015 |
G10150 |
S15C |
C15E |
1.0401 |
C15E4 |
Ck15 |
1.1141 |
|||||
20 |
1020 |
G10200 |
S20C |
C22E |
1.0402 |
C20E4 |
Ck22 |
1.1151 |
|||||
25 |
1025 |
G10250 |
S25C |
C25E |
1.1158 |
C25E4 |
Ck25 |
||||||
30 |
1030 |
G10300 |
S30C |
C30E |
1.1178 |
C30E4 |
Ck30 |
||||||
35 |
1035 |
G10350 |
S35C |
C35E |
1.1181 |
C35E4 |
Ck35 |
||||||
40 |
1040 |
G10400 |
S40C |
C40E |
1.1186 |
C40E4 |
Ck40 |
||||||
45 |
1045 |
G10450 |
S45C |
C45E |
1.1191 |
C45E4 |
Ck45 |
||||||
50 |
1050 |
G10500 |
S50C |
C50E |
1.21 |
C50E4 |
Ck50 |
||||||
55 |
1055 |
G10550 |
S55C |
C55E |
1.1203 |
C55E4 |
Ck55 |
Cast steel comparison (or equivalent) |
||||||
China |
United States |
Japan |
Germany |
|||
China, GB |
ASTM |
AISI/UNS |
SAE |
JIS |
Din |
W-Nr. |
20 |
1020 |
G10200 |
1020 |
S20C |
Ck22 |
1.1151 |
S20CK |
||||||
45 |
1045 |
G10450 |
1045 |
S45C |
Ck45 |
1.1191 |
65Mn |
1566 |
G15660 |
1566(1066) |
S58C |
65M4 |
– |
20Cr |
5120 |
G51200 |
5120 |
SCr420 |
20Cr4 |
1.7027 |
40Cr |
5140 |
G51400 |
5140 |
SCr440 |
41Cr4 |
1.7035 |
35CrMo |
4135 |
G41350 |
4135 |
SCM435 |
34CrMo4 |
1.7220 |
42CrMo |
4140 |
G41400 |
4140 |
SCM440 |
42CrMo4 |
1.7225 |
40CrNiMo |
4340 |
G86200 |
8620 |
SNCM439 |
36CriNiMo4 |
1.6511 |
GCr15 |
5210 |
G52100 |
5210 |
SUJ2 |
100Cr6 |
1.3505 |
1Cr18Ni9Ti |
– |
– |
– |
– |
X10CrNiTi18 9 |
1.4541 |
Cast malleable iron comparison (or equivalent) |
||||
China GB/T9440-1988 |
ASTM A47 |
Japan JIS |
Germany |
ISO Standard |
DIN(W-Nr.) |
||||
KTH300-06 |
– |
FCMB30-06 |
– |
B30-06 |
FCMB27-05 |
||||
KTH330-08 |
22010 |
FCMB31-08 |
– |
– |
KTH350-10 |
32510 |
FCMB35-10 |
GTS-35-10 0.8135 |
B35-10 |
KTH370-12 |
35018 |
(FCMB37) |
– |
– |
Cast ductile iron comparison (or equivalent) |
||||||
China GB/T1348-1988 |
ASTM A536-99 |
UNS |
Japan JIS |
Germany |
ISO1083:1987 |
|
Din |
W-Nr. |
|||||
QT400-18 |
60-40-18 |
F32800 |
FCD400-18 |
GGG-40 |
0.7040 |
400-18 |
QT400-15 |
60-42-10 |
– |
FCD400-15 |
GGG-40 |
0.7040 |
400-15 |
QT450-10 |
65-45-12 |
F33100 |
FCD450-10 |
– |
– |
450-10 |
QT500-7 |
70-50-05 |
– |
FCD500-7 |
GGG-50 |
0.7050 |
500-7 |
QT600-3 |
80-60-03 |
– |
FCD600-3 |
GGG-60 |
0.7060 |
600-3 |
Cast gray iron comparison (or equivalent) |
|||||||
China GB/T 9439-1988 |
ASTM A159-82 |
UNS |
ASTM A48-00 |
Japan JIS |
Germany |
ISO Standard |
|
Din |
W-Nr. |
||||||
HT100 |
– |
– |
– |
FC100 |
GG10 |
0.6010 |
100 |
HT150 |
G1800 |
F11701 |
No. 20 |
FC150 |
GG15 |
0.6015 |
150 |
HT200 |
G2500 |
F12101 |
No. 30 |
FC200 |
GG20 |
0.6020 |
200 |
HT250 |
G3000 |
F12401 |
No. 35 |
FC250 |
GG25 |
0.6025 |
250 |
F12801 |
No. 40 |
||||||
HT300 |
G3500 |
F13301 |
No. 45 |
FC300 |
GG30 |
0.6030 |
300 |
HT350 |
G4000 |
F13501 |
No. 50 |
FC350 |
GG35 |
0.6035 |
350 |
Die casting alloy properties |
Aluminum die casting alloys |
Zinc-aluminum cast alloys |
Zinc casting alloys |
Magnesium die casting alloys |
||||||||
|
A360 |
A380 |
A383 |
A413 |
ZA-8 |
ZA-27 |
Zamak 3 |
Zamak 5 |
AZ91D |
AM60B |
AM50A |
AZ63 |
Ultimate Tensile Strength, MPa (ksi) |
300 (44) |
317(46) |
310(45) |
296 (43) |
374(54.2) |
426(61.8) |
285(41.3) |
328(47.6) |
230(33.4) |
24(35) |
228(33) |
275(39.9) |
Tensile Yield Strength, MPa (ksi) |
170 (24.7) |
159(23) |
152 (22) |
145 (21) |
290(42.1) |
371(53.8) |
|
|
150(21.8) |
131(19) |
124(18) |
130(18.9) |
Elongation (% in.2 in.) |
2.5 |
2.5 |
3.5 |
2.5 |
8 |
2.5 |
10 |
7 |
3 |
13 |
15 |
5 |
Shear Strength, MPa (ksi) |
190 (28) |
195 (28) |
187 (27) |
170 (25) |
275(39.9) |
325(47.1) |
215(31.2) |
262(38) |
140(20) |
241(35) |
228 (33) |
145(21) |
Hardness, Brinell |
75 |
80 |
75 |
80 |
103 |
119 |
82 |
91 |
63 |
65 |
60 |
73 |
Thermal Conductivity, |
113 (784) |
109 (756) |
96.2(668) |
121 (840) |
115(798) |
125(868) |
113(784) |
62.9(437) |
72.7(505) |
61(423) |
65(451) |
61(423) |
Density, g/cc (lb/in³) |
2.68(0.097) |
2.76 (0.1) |
2.70(0.098) |
2.66(0.0961) |
6.3(0.228) |
5.02(0.181) |
6.6(0.238) |
6.6(0.24) |
1.8(0.0654) |
1.8(0.0650) |
1.77(0.0639) |
1.83(0.0661) |
Chemical Properties |
|
|
|
|
|
|
|
|
|
|
|
|
Aluminum, Al |
85.1-90.6% |
79.6-89.5% |
79.7-88.5% |
82.2-89.0% |
8% |
27% |
4.10% |
4.20% |
8.5%-9.5% |
5.6%-6.4% |
4.5%-5.3% |
5.3%-6.7% |
Copper, Cu |
<=0.60% |
3.0-4.0% |
2.0-3.0% |
<=1.0% |
|
2.20% |
|
|
<=0.025 |
<=0.008 |
<=0.008 |
<=0.02 |
Iron, Fe |
<=2.0% |
<=2.0% |
<=1.30% |
<=2.0% |
|
|
|
|
<=0.004 |
<=0.004 |
<=0.004 |
<=0.003 |
Magnesium, Mg |
0.40 -0.60% |
<=0.10% |
<=0.10% |
<=0.10% |
0.02% |
0.02% |
0.04% |
0.03% -0.06% |
|
|
|
|
Manganese, Mn |
<=0.35% |
<=0.50% |
<=0.50% |
<=0.35% |
|
|
|
|
0.17%-0.4% |
0.26%-0.5% |
0.28%-0.5% |
0.15%-0.17% |
Nickel, Ni |
<=0.50% |
<=0.50% |
<=0.30% |
<=0.50% |
|
|
|
|
<=0.001% |
<=0.001% |
<=0.001% |
<=0.002% |
Other, total |
<=0.25% |
<=0.50% |
<=0.50% |
<=0.25% |
|
|
|
|
|
|
|
|
Silicon, Si |
9.0-10.0% |
7.50-9.50% |
9.50-11.5% |
11.0-13.0% |
|
|
|
|
<=0.08% |
<=0.08% |
<=0.08% |
<=0.1% |
Tin, Sn |
<=0.15% |
<=0.35% |
<=0.15% |
<=0.15% |
|
|
|
|
|
|
|
|
Zinc, Zn |
<=0.50% |
<=3.0% |
<=3.0% |
<=0.50% |
91% |
71% |
96% |
95% |
0.45% -0.9% |
<=0.2% |
<=0.2% |
2.5%-3.5% |
Quality Management System Certificate